First acrylic fountain pen

Margo

Full Member
Joined
May 25, 2020
Posts
73
Location
England
First Name
Margo
Turned my first in acrylic, second ever fountain pen today!
Executive model, can't remember the name of the blank, if it even came with one! :whistling:
 

Attachments

  • IMG_20200531_185738.jpg
    IMG_20200531_185738.jpg
    100.9 KB · Views: 146

Margo

Full Member
Joined
May 25, 2020
Posts
73
Location
England
First Name
Margo
Hi Phil,
I use micromesh, then a couple of coats of CA glue (this went wrong on one part and had to be taken off again!)
Then a wipe or two of burnishing cream.

I have been advised that burnishing cream is better than tcut car polish, which I did previously! It is, though I'm not sure if I'm doing it right... Wipe it on, turn the lathe on slowish and polish, using an old tack cloth.
 

Phil Dart

Moderator
Executive Member
Joined
Nov 28, 2014
Posts
5,455
Location
Colebrooke, Devon
First Name
Phil
You don't need to bother with the CA Margo. Get a good finish with abrasives, so that you don't have any tooling marks or radial marks showing. I always give it a good going over with 0000 wire wool too (along the length, with the lathe stopped), as a last abrasive process. Then you can get to work with the burnishing cream.

Yes, Tcut is quite coarse - burnishing cream is much finer, but by putting on CA, you are introducing a medium which firstly, unless you de-nib it and go though a fine abrasive routine again, will cause imperfections over the top of an already perfect surface, secondly is un-necessary since the surface doesn't need sealing, thirdly, will only sit on the surface rather than integrate with it as it might with wood, and therefore may well flake or chip in time, and fourthly, won't shine any more than by omitting it and just using burnishing cream.

Use a clean tissue to wipe off the cream though, in preference to a tack cloth. Rather than just wiping it on, work it in, and work at it with the lathe running like you would an abrasive, which is what it in fact is. Take it off with the clean tissue, and keep turning it to a clean part until all the blackening is removed. There's no harm in repeating the process as many times as you need to. You need to burnish at a sort of medium speed. There are those that do everything at the fastest possible speed, but you'll get a better, more even shine if you slow it down to maybe 1500 - 1800rpm. Fastest isn't always best, and certainly slow is no good for burnishing.

I hope that helps
 

Bill Mooney

Blind old git
Grand Master
Joined
Aug 16, 2014
Posts
10,997
Location
County Durham
First Name
Bill
I agree with Phil. I sand at 900-1000 rpm & burnish at 1500-1600 tpm. Any faster & the speed throws the polish off as fact as you try to apply it. Like Phil my last abrasive is 0000 wire wool.
A lovely pen by the way. Well done.:thumbs:
 